Wet-spun polyacrylonitrile/H۲O precursor fiber with enhanced thermal properties and graphitic order

سال انتشار: 1400
محل انتشار: چهارمین کنفرانس بین المللی توسعه فناوری در مهندسی شیمی
کد COI اختصاصی: CHEMISB04_026
زبان مقاله: انگلیسی
تعداد مشاهده: 295

نویسندگان

Chemical Engineering Department, University of Kashan, ۸۷۳۱۷۵۳۱۵۳ Kashan, Iran

چکیده

Polyacrylonitrile (PAN) fibers with unique properties are becoming increasingly crucial as precursors for the fabrication of carbon fibers. Here, we recommend providing PAN fiber to improve the homogeneity and thermal stability of the fibers. Adding a prearranged amount of water (۴ vol.%) as nonsolvent to the PAN solution, followed by wet spinning, has prepared precursor fiber with high thermal properties and unique graphitic order. Differential scanning calorimetry (DSC) and Thermogravimetric analysis (TGA) results illustrate that PAN/H۲O precursor fiber has higher thermal decomposition temperature, enhanced residual weight, and diminished heat release rate, a promising precursor for the evolution of high-performance composite fibers.

کلیدواژه ها

wet spinning, polyacrylonitrile fiber, thermal properties, nonsolvent

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.