Influence of Al۲O۳ Additive on Mechanical Properties of Wollastonite Glass-Ceramics

  • سال انتشار: 1400
  • محل انتشار: مجله بین المللی طراحی پیشرفته و تکنولوژی ساخت، دوره: 14، شماره: 3
  • کد COI اختصاصی: JR_ADMTL-14-3_004
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 227
دانلود فایل این مقاله

نویسندگان

Monavvar Rahimi

Department of Chemistry, Islamic Azad University, North Tehran Branch, Tehran, Iran

Babak Sadeghi

Department of Chemistry, Islamic Azad University, Tonekabon Branch, Tonekabon, Iran

Maryam Kargar Razi

Department of Chemistry, Islamic Azad University, North Tehran Branch, Tehran, Iran

چکیده

In this paper, wollastonite glass-ceramics and composites of wollastonite glass– ceramics with ۲.۵, ۵, ۱۰ and ۲۰ weight percent alumina with an average size of ۲ microns and also wollastonite glass-ceramics with ۲.۵, ۵, and ۱۰ percent alumina with an average size of ۴۰ nanometers were produced without pressure by Sintering and their physical properties (e.g. bulky density, the percentage of linear shrinkage and relative density) were measured. Sinter operation in the temperature range of ۱۰۳۰-۱۱۷۰ °С was performed for ۳ hours. Existing phases in composites by X-ray Diffraction (XRD) and their structure were examined by Scanning Electron Microscopy (SEM) and while measuring mechanical properties of composites such as flexural strength, hardness and compared fracture toughness with base glass ceramic was performed. Results indicate that adding ۲.۵ percent micron-sized alumina to wollastonite glass-ceramics decreases the flexural strength from ۸.۰۱±۱۲۰ to ۱۰.۲۶±۵۰ MPa and its fracture toughness declines to ۰.۸±۰.۷۴, while by adding ۲.۵ percent nano-alumina to wollastonite glass – ceramics, the flexural strength increases from ۸.۰۱±۱۲۰ to ۲۰.۷±۱۳۳ MPa and its fracture toughness improves up to ۱.۴۰±۱۰.

کلیدواژه ها

Glass-Ceramic Composite, Nano-Alumina, Mechanical Properties, Sintering, Thermal properties, Wollastonite

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.