Structural, Magnetic and Electromagnetic Absorption Properties of SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹/BaTiO۳ Nanocomposites Prepared By Sol- Gel Auto Combustion Method
محل انتشار: فصلنامه شیمی نوین، دوره: 8، شماره: 4
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 173
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJNC-8-4_007
تاریخ نمایه سازی: 26 مهر 1400
چکیده مقاله:
In this research, first, nanoparticles of SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹ hexaferrite was synthesized via sol-gel autocombustion process and then the nanocomposites of hexagonal ferrites/perovskite with the amounts of SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹ /BaTiO۳ (۵۰/۵۰, ۴۰/۶۰, ۷۰/۳۰ w/w) was prepared by ball-milling method. FTIR spectra were shown that the bands at about ۴۰۰ and ۵۰۰ cm-۱ proved the formation of hexagonal ferrites. XRD analysis was confirmed the formation of hexaferrite and perovskite phase of BaTiO۳. FESEM pictures was represented the formation of hexagonal nanoparticles and sphere shape of BaTiO۳. VSM hysteresis loop was revealed that SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹ belonged to the soft magnetic materials due to the ۶۰۴.۴۵Oe coercivity. By formation of nanocomposites the coercivity was increased up to ۱۵۰۰ Oe. VNA analysis was VNA analysis revealed that the maximum absorption of -۱۶.۴db at ۱۱.۵ GHz frequency for SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹ /BaTiO۳ (۶۰/۴۰) nanocomposite. Microwave absorption properties of samples was investigated by (vector network analyzer) VNA. The maximum value of reflection loss was --۱۶.۴db at ۱۱.۵ GHz frequency for SrFe۱۱.۹۸Mg۰.۱Sn۰.۱O۱۹ /BaTiO۳ (۶۰/۴۰) nanocomposite.
کلیدواژه ها:
نویسندگان
kamelia Ghaffarzadeh
Department of Chemistry, Tehran North Branch, Islamic Azad University, Tehran, Iran
pirouz derakhshi
Department of Chemistry, Tehran North Branch, Islamic Azad University, Tehran, Iran
Mohammad Yousefi
Department of Chemistry, Yadegar-e Imam Khomeini (RAH) Shahr-e Rey Branch, Islamic Azad University, Tehran, Iran
ali mahmoudi
Department of Chemistry, Tehran North Branch, Islamic Azad University, Tehran, Iran
parviz aberoomand azar
Department of Chemistry, Science and Research Branch, Islamic Azad University, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :