Influence of Initial Microstructure on Hot Deformation Behavior of Duplex Stainless Steels
- سال انتشار: 1392
- محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 1، شماره: 2
- کد COI اختصاصی: JR_JMATPR-1-2_007
- زبان مقاله: انگلیسی
- تعداد مشاهده: 208
نویسندگان
Department of Materials Engineering, Esfarayen University, Esfarayen, Iran
School of Materials Engineering, Sahand University of Technology, Tabriz, Iran
Department of Material Engineering, Ferdowsi University of Mashhad, Mashhad, Iran
Department of Materials Engineering, Esfarayen University, Esfarayen, Iran
چکیده
In this research the effect of initial microstructure on hot deformation behavior in terms of Ferrite-to-Austenite ratios is studied. Two types of stainless steels C۱ and C۲ were homogenizing heat-treated and deformed under hot compression examinations at temperatures ۹۰۰ºC and ۱۱۰۰ºC at strain rate of ۰.۱s-۱. The results showed that the flow stress levels of specimens are strongly related to deformation parameters and initial microstructures of steels. Moreover, during cooling from ۱۳۵۰ºC to the deformation temperature, flow stress level increased for both samples because of increment in austenite content.کلیدواژه ها
Duplex stainless steel, Hot compression, Flow curves, Dynamic recovery, Dynamic recrystallizationاطلاعات بیشتر در مورد COI