Inspection of Ultrasonic Welded Parts Made of Glass Fiber Reinforced Plastics by Active Thermography Method
- سال انتشار: 1399
- محل انتشار: هفدهمین همایش ملی و ششمین کنفرانس بین المللی مهندسی ساخت و تولید
- کد COI اختصاصی: ICME17_200
- زبان مقاله: انگلیسی
- تعداد مشاهده: 257
نویسندگان
MSc Student of Mechanical Engineering, Tarbiat Modares University/Faculty of Mechanical Engineering.
Assistant Professor, Tarbiat Modares University/Faculty of Mechanical Engineering.
Ph.D. Student, Faculty of Mechanical Eng., Tarbiat Modares University, Tehran, Iran
MSc, Faculty of Mechanical Eng., Tarbiat Modares University, Tehran, Iran
چکیده
Ultrasonic welding is considered as a rapid joining process. Recently application of this method in joining of polymeric parts is increasing. Applicability of this method in joining of thermoplastic materials is confirmed by many researchers. However a few researches have been conducted on applicability of ultrasonic method in joining of thermosets. On the other hand ultrasonic welding of polymeric welded materials specially thermosets may have challenges. One of the major challenges could be the existence of various defects such as detachments, voids and incomplete fusion. Consequently ultrasonic welding of polymeric parts shall be continued by inspections. Numerous nondestructive testing (NDT) methods are introduced to inspection of polymer-based materials. Active IR Thermography is one of the well-known NDT methods in inspection of polymer based materials and polymer-based composites. Therefore it can be used to inspection of welded polymeric parts. In present research two polymeric parts made of glass fiber reinforced epoxy were joined by ultrasonic welding. At the next stage IR thermography was employed to inspection of welded parts with artificial defects and the applicability of IR thermography in detection of various types of defects were investigated.کلیدواژه ها
Ultrasonic welding, Thermography, Glass Fiber Reinforced Plastic (GFRP),مقالات مرتبط جدید
- اصول طراحی مفهومی پس سوز یک موتور توربوفن سنگین
- مطالعه تجربی و عددی توزیع ضخامت در فرم دهی افزایشی تک نقطه ای یک جسم مخروطی
- پیشبینی و بررسی ویژگیهای آیرودینامیکی پرتابه ای چرخان با استفاده از دینامیک سیالات محاسباتی
- تحلیل عددی کنترل جریان آشفته حول استوانه با استفاده از دو استوانه ی کنترلی دیگر
- مطالعه عددی اثر جایگزینی نیتروژن با دی اکسید کربن بر احتراق موتور دیزل
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.