Inspection of Carbon Fiber Reinforced Composites with Planar and Crack Defects by Active Thermography Method

  • سال انتشار: 1399
  • محل انتشار: هفدهمین همایش ملی و ششمین کنفرانس بین ­المللی مهندسی ساخت و تولید
  • کد COI اختصاصی: ICME17_164
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 261
دانلود فایل این مقاله

نویسندگان

Pouya Faraji Kalajahi

Ph.D. Student, Faculty of Mechanical Eng., Tarbiat Modares University, Tehran, Iran

Davood Akbari

Asstistant Professor, Faculty of Mechanical Eng., Tarbiat Modares University, Tehran, Iran

Milad Mohammadian

MSc, Faculty of Mechanical Eng., Tarbiat Modares University, Tehran, Iran

Mohamad Tizmaghz Nejad

MSc Student, Faculty of Mechanical Eng., Tarbiat Modares University, Tehran, Iran

چکیده

Carbon fiber reinforced composites (CFRPs) are used in various fields such as automotive, aerospace, offshore structures, oil and gas industry and marine. Presence of defects such as cracks, delamination and detachment could affect on the mechanical and chemical properties of these materials and reduce the strength of the structures. Consequently in order to ensure the proper performance of fabricated parts, Nondestructive testing (NDT) shall be employed. Among the thermography methods of composites, IR thermography is well-known. In present research Active IR Thermography was employed in order to inspect of carbon fiber reinforced composites (CFRPs). CFRP samples prepared by hand lay-up method. Two types of defects including planar defect and crack were created on the samples. At first stage planar defects were selected in three different size. At the next stage planar defects were placed in three different depths with the same size. Cracks were created on the samples by means of a riser with two different lengths. Active Thermography was performed in transmission mode. Optical excitation was conducted by employing a high power Flash lamp. Thermal images obtained for all samples. Results indicated proper capability of active thermography in inspection of carbon fiber reinforced composites.

کلیدواژه ها

Carbon Fiber Reinforced Composites, Active Thermography, Crack, Planar Defect

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.