Evaluation of the Polymerization Properties of Bulk-Fill Composite Resins

  • سال انتشار: 1400
  • محل انتشار: مجله مواد و تکنیک های دندانپزشکی، دوره: 10، شماره: 3
  • کد COI اختصاصی: JR_JDMT-10-3_006
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 135
دانلود فایل این مقاله

نویسندگان

Latife Altınok Uygun

Department of Restorative Dentistry, Faculty of Dentistry, Afyonkarahisar Health Sciences University, Afyonkarahisar, Turkey.

Nilgün Akgül

Department of Restorative Dentistry, Faculty of Dentistry, Pamukkale University, Denizli, Turkey.

چکیده

Introduction: The aim was to evaluate the polymerization properties of bulk-fill composite resins in terms of the degree of conversion (%DC), Vickers hardness (HV). SonicFill (SF, Kerr, CA, USA), Tetric Evo Ceram Bulk-Fill (TECBF, Ivoclar Vivadent Schaan, Lichtenstein), and X-trafil (XTF, Voco GmbH, Cuxhaven, Germany) were investigated. Methods: The samples prepared from composites (n = ۱۰)  were polymerized via three different curing modes (standard mode: ۲۰ s, high-power mode: ۱۲ s, extra power mode: ۶ s) using a polywave LED. %DC was determined by FTIR-ATR-spectroscopy. HV was measured at the top and bottom of the specimens. Data were analyzed by two way ANOVA, and Bonferroni’s post-hoc respectively (α=۰.۰۵). Results: Except TECBF (%۴۱.۱۰ ± ۳.۱) in three different curing modes, all materials showed no significant inferior %DC. In all curing modes, the highest hardness ratio was found in XTF (۰.۸۴ ± ۰.۰۳ GPa), and the lowest hardness ratio was found in the TECBF (۰.۷۸ ± ۰.۰۲GPa). In the cases where the extra power mode of the Valo Led was applied, the lowest degree of conversion and hardness were also measured. Conclusion: It has been observed that the examined properties of some tested materials change with the curing time and power of the light and however, the results are dependent on the material.Extra power mode of the Valo Led negatively affected high viscosity bulk-fill composites in terms of their polymerization properties

کلیدواژه ها

Bulk-fill, resin composite, light curing, degree of conversion, vickers hardness

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.