Effect of Accumulative Roll Bonding Process on Mechanical Properties of Al-Based Composite Reinforced with Nano-Trioxide Tungsten
- سال انتشار: 1400
- محل انتشار: چهارمین کنفرانس بین المللی توسعه فناوری مهندسی مواد، معدن و زمین شناسی
- کد COI اختصاصی: EMGBC04_074
- زبان مقاله: انگلیسی
- تعداد مشاهده: 473
نویسندگان
Faculty of Materials and Metallurgical Engineering, Semnan University, Semnan, Iran
R&D Department, Oghab Afshan Industrial & Manufacturing Company, Semnan, Iran
چکیده
In the present study, an Al/WO۳p metal matrix nanocomposite was fabricated by accumulative roll bonding (ARB) technique. Mechanical properties of specimens were investigated by microhardness and tensile test. Several factors that affect uniform distribution particles were investigated. After ۱۲ ARB cycles, a nanocomposite with a uniform distribution of nanoparticles was produced. It was shown that the tensile strength of the ARBed composite enhanced with the increasing number of ARB cycles. After the first cycle, a significant increase was observed in the tensile strength of nanocomposite in ۲.۰ percent volume of WO۳p, from ۸۹ MPa to ۱۲۸ MPa (almost ۱.۴ times increase in strength). After the final cycle, the tensile strength value increased to ۲۰۵ MPa (that is almost ۲.۳ times increase in strength) due to the strain hardening and grain refinement. The X-ray diffraction results showed that Al/WO۳p nanocomposite with the average crystallite size of ۴۱ nm was successfully attained after ۱۲ cycles of the ARB process. Finally, observations revealed that the fracture mode in Al/WO۳p nanocomposite was of type shearing ductile fracture with elongated shallow dimples.کلیدواژه ها
Accumulative Roll Bonding, Nanocomposite, Microstructure, Mechanical Propertiesمقالات مرتبط جدید
- محاسبه تخلخل و نحوه توزیع آن به کمک نمودار تصویرگر FMI
- تفسیر نمودار تصویرگر FMI به منظور شناسایی شکستگیهای دیواره چاه
- ارزیابی تاثیر تکانه قیمتی سوخت های مصرفی بر میزان مصرف
- بررسی تنشهای دیواره چاه و محاسبه فشار منفذی از نمودارهای چاهپیمایی معمول و تصویرگر FMI
- Chelating Agents and their role in enhancing carbonate rock dissolution: A critical Review
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.