Age-Hardening Behavior and the Related Changes in a Silver-Copper-Palladium Alloy
- سال انتشار: 1399
- محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 8، شماره: 2
- کد COI اختصاصی: JR_JMATPR-8-2_004
- زبان مقاله: انگلیسی
- تعداد مشاهده: 209
نویسندگان
Metallurgy and Materials Engineering Department, Golpayegan University of Technology, Golpayegan, Iran
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Department of Materials science and Engineering, Hamedan University of Technology, Hamedan, Iran
چکیده
Age-hardening behavior and related changes were studied to elucidate the hardening mechanism of an Ag–Cu–Pd alloy by Differential Scanning Calorimetry (DSC), hardness test, X-ray diffraction (XRD), scanning electron microscopic (SEM) observations and energy dispersive spectrometer (EDS). The results showed that hardness of the alloy was raised to ۹۰% and ۶۸% of its solution state value by isothermal aging at ۳۰۰ ◦C and ۴۰۰ ◦C, respectively. However, aging at ۵۰۰ ◦C led to a decrease in the hardness of the alloy. Moreover, while age hardening at ۳۰۰ ◦C occurred due to coherency strains between the (۱۱۱) plane of Ag-rich and the (۱۱۱) plane of Cu۳Pd phases, the mechanism of aging at ۴۰۰ ◦C was the formation of Cu۳Pd superlattice with the L۱۲-type crystal structure. In contrast, reduction of Cu۳Pd phase and formation of Cu solid solution decreased hardness during aging at ۵۰۰oC.کلیدواژه ها
Ag-Cu-Pd alloys, Age-hardening, Scanning Electron Microscopy, X-ray diffractionاطلاعات بیشتر در مورد COI