Stress intensity factor evaluation for fatigue crack in working roll due to hot rolling process

سال انتشار: 1399
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 261

فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:


تاریخ نمایه سازی: 25 خرداد 1400

چکیده مقاله:

Crack growth is one of the main causes of failure of hot rolling rollers, which also causes damage to other parts. For this reason, three-dimensional modeling of surface crack, the study of the effect of different factors and different phenomena on roller fatigue life and the effect of stress distribution are important research topics. To increase the efficiency of rollers and propose practical methods, in this study, the stress intensity factors of surface cracks in rollers fabricated from High Chromium Steel (HCS) in the hot rolling process are modeled in three dimensions. Each component modeled separately, the complexity of problem solving is reduced and the speed of solution is improved using the proposed method. In this regard, first, the types of cracks and their causes in the roller as well as the effect of residual stresses on the roller are analyzed. By selecting HCS roller and sheet, modeling and stress analysis are performed by finite element method. In addition, the boundary element method was used to simulate the three-dimensional cracks and the stress intensity factors. The results show that the values of stress intensity factors at the deepest point of the crack front are maximum.


Reza Masoudi Nejad

School of Mechanical and Electrical Engineering University of Electronic Science and Technology of ChinaChengdu, China

Peyman Noroozian Rizi

Department of Mechanical Engineering Foolad Institute of Technology Fooladshahr, Isfahan, Iran

Greg Wheatley

College of Science and Engineering James Cook University Townsville, Australia

Hosein Ghasemi

Department of Mechanical Engineering University of Birjand Birjand, Iran