Fracture Mode of Opening for Annular Crack in Anisotropic Composites
- سال انتشار: 1399
- محل انتشار: هفتمین کنفرانس بین المللی مواد کامپوزیتی: ساخت، خواص و کاربرد
- کد COI اختصاصی: COMPOSIT07_028
- زبان مقاله: انگلیسی
- تعداد مشاهده: 156
نویسندگان
Assistant Professor, School of Engineering, University Tehran, Tehran, Iran
MS Graduate, School of Civil Engineering, University of Tehran, Tehran, Iran
چکیده
The existence and extension of the cracks in anisotropic composites is one of the issues to be considered in fracture mechanics to prevent the devastating effects of cracks. Cracks can be subjected to different types of fracture modes that considering these modes is essential to predict the behavior of cracks. This paper investigates the effects of the fracture mode of opening on the annular crack in an anisotropic composite. By substituting the boundary conditions into governing equations of the medium, the problem reduced to triple integral equations. With the aid of Hankel and Abel integral transforms, the triple integral equations reduced to two Fredholm’s integral equations which are amenable to numerical solutions. The inner and outer stress intensity factors of the annular crack are obtained. From the results, it can be concluded that the stress intensity factor (SIF) are independent of material properties.کلیدواژه ها
Composite, anisotropy, annular crack, stress intensity factorمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.