Mechanical Properties of PP/PE/Clay Nanocomposites
- سال انتشار: 1399
- محل انتشار: هفتمین کنفرانس بین المللی مواد کامپوزیتی: ساخت، خواص و کاربرد
- کد COI اختصاصی: COMPOSIT07_025
- زبان مقاله: انگلیسی
- تعداد مشاهده: 202
نویسندگان
PhD, Technical and Engineering Faculty, University of Bonab, Bonab, Iran
M.Sc , Technical and Engineering Faculty, University of Bonab, Bonab, Iran
M.Sc, Snowa Eps Company, Assaluyeh, Iran
PhD, Department of Polymer engineering, Azarbaijan Shahid Madani university, Tabriz, Iran
چکیده
Polypropylene (PP)/ high density polyethylene (HDPE) blend nanocomposites were prepared using an internal mixer. One commercial organo-montmorillonite (۲۰A) and one maleated polymer (PP-g-MA) served as the reinforcing filler and compatibilizer, respectively. Four different blending sequences were studied. The results showed that clay in all the nanocomposites had a tendency to distribute in matrix phase or interface and formed the intercalated structure when PP-g-MA was presented. The tensile modulus of PP/HDPE blends increased after adding C۲۰A. Specifically, there was a synergistic effect of PP-g-MA and clay in improving the particles size distribution in some nanocomposites. The results also show that the degree of the synergistic compatibilizing effect was dependent on the nanocomposite preparation condition such as blending sequences and rotor speed during preparing of the nanocomposites.کلیدواژه ها
Polypropylene , high density polyethylene , montmorillonite, nanocompositesمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.