Hot Workability and Processing Map of High Gd Content Mg-Gd-Zn-Zr-Nd Alloy
- سال انتشار: 1400
- محل انتشار: مجله شکل دهی مواد، دوره: 8، شماره: 2
- کد COI اختصاصی: JR_IJMF-8-2_006
- زبان مقاله: انگلیسی
- تعداد مشاهده: 354
نویسندگان
Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran, Iran
Faculty of Materials Science and Engineering, K. N. Toosi University of Technology, Tehran, Iran
Department of Materials Science and Engineering, University of Bonab, Bonab, Iran
چکیده
Hot workability of as-extruded high Gd content Mg-۵Gd-۰,۵Zn-۰.۵Zr-۲.۵Nd alloy was investigated using the hot compression test in a temperature range of ۳۰۰-۵۰۰ °C and strain rates of ۰.۰۰۱-۱s-۱. Hot workability assessment was conducted by capturing microstructural evolution of high temperature deformed samples, and by constructing power dissipation and instability maps. Using experimental data of hot compression tests, the power dissipation map of the alloy was constructed, in which a domain of dynamic recrystallization (DRX) occurred at the temperature range of ۳۵۰-۴۵۰ °C and strain rate of ۰.۰۰۱-۰.۱ s-۱, representing the optimum hot working window. Furthermore, the processing map of the alloy was constructed, and flow instability regions were also indicated based on the Ziegler's flow instability criterion.کلیدواژه ها
Magnesium alloy, Rare earth metals, Processing map, Hot workabilityاطلاعات بیشتر در مورد COI