Intermetallic phase formation during combustion synthesis of mechanically activated Ni-Ti alloy

  • سال انتشار: 1393
  • محل انتشار: مجله بین المللی طراحی پیشرفته و تکنولوژی ساخت، دوره: 7، شماره: 4
  • کد COI اختصاصی: JR_ADMTL-7-4_001
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 362
دانلود فایل این مقاله

نویسندگان

Seyed Khatiboleslam Sadrnezhaad

Sharif University of Technology

Shahin Katiraei

Abbas Ghasemi

چکیده

Intermetallic phase formation and oxidation reaction during combustion synthesis (CS) of Ni-Ti equiatomic mixture are affected by mechanical activation (MA) and pre-heating conditions. Important parameters are ignition time, reaction duration, temperature rise, microstructural change, titanium oxidation and intermetallic phase formation. Superelasticity and shape memory effects are influenced by two-stage austenite-rhombohedral and rhombohedral-martensite transformations detected by differential scanning calorimetry (DSC) and scanning electron microscopy (SEM) of the combusted samples. Tension tests indicated superelastic behavior after ۱ h, production of Ni۳Ti after ½ h and delayed superelastic/thermoelastic behavior after ۲ h MA. Results indicate that pre-combustion heating fosters mono-phase formation and titanium oxidation; while mechanical activation lowers ignition-start-time, synthesis-duration and Ni۳Ti formation.

کلیدواژه ها

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.