Enhanced electroconductivity of cotton fabric by RGO/TiO۲/cotton
سال انتشار: 1399
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 269
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
SDNCONF04_002
تاریخ نمایه سازی: 15 اردیبهشت 1400
چکیده مقاله:
In this study, graphene/TiO۲ nanocomposite was used to enhance the electroconductivity of cotton fabric. A simple dip-coating method was applied to load graphene oxide on the surface of cotton fabric. For reducing the graphene oxide and fabricating nanocomposite of reduced graphene oxide (RGO)/TiO۲, TiCl۳ aqueous solution was used as a reducing agent and precursor. So, to complete the process of fabrication, the fabric included graphene oxide was immersed in TiCl۳ solution. The process is shown in figure ۱. Microstructure and morphology of samples were characterized by SEM images and Raman spectroscopy. Electrical resistivity was also measured using the two prob multimeter. The nanocomposite of the RGO/TiO۲/cotton fabric increased the electrical conductivity of fabric which was due to the presence of graphene as expected.
کلیدواژه ها:
Graphene oxide ، Conductive cotton fabric ، Reduced graphene oxide (RGO)/TiO۲/cotton fabric ، graphene ، TiO۲