Investigating the heat input effect of the GTAW process upon the microstructure and HAZ extension of HSLA-۱۰۰ steel weld joints using thermal cycles
- سال انتشار: 1399
- محل انتشار: مجله ی بین المللی انجمن آهن و فولاد ایران، دوره: 17، شماره: 1
- کد COI اختصاصی: JR_ISSIRAN-17-1_006
- زبان مقاله: انگلیسی
- تعداد مشاهده: 239
نویسندگان
material science and engineering department, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
material science and engineering department, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
material science and engineering department, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
چکیده
In the current research, the welding of HSLA-۱۰۰ steel was accomplished with three different heat inputs using the GTAW process. The microstructure of various joint zones was investigated utilizing an optical microscope and scanning electron microscope. For the purpose of assessing the impact of thermal cycles upon the extension and alterations in the heat-affected zone, the thermocouples were placed at distinct distances from the fusion line. The results indicated that the weld metal microstructure comprised of acicular ferrite and a number of polygonal and quasi-polygonal Ferrite with M/A constituent. An epitaxial growth was observed in the fusion line in all heat inputs. It was determined that the heat-affected zone microstructure consisted of two regions, namely a coarse-grained heat-affected zone with a granular and lath bainite microstructure and a fine-grained heat-affected zone with the prevailing microstructure of granular Bainite. The results indicated that increasing the heat input leads to a decrease in the amount of acicular ferrite and M/A constituent volume fraction in the weld metal and an increase in lath bainite in coarse-grained zone. It was found that by increasing the heat input from ۰.۷۸kJ/mm to ۱.۴۲ kJ/mm, the grain size increases from ۲۹.۲μm to ۷۶.۵ μm and from ۱۵.۷μm to ۳۲.۵μm in coarse-grained and fine-grained zone, respectively. The thermal cycles evaluation pertinent to the implanting of a thermocouple disclosed that the heat-affected zone width is extended from ۳.۶ mm to ۴.۵mm by increasing the heat input from ۰.۷۸kJ/mm to ۱.۴۲ kJ/mm.کلیدواژه ها
HSLA-۱۰۰ steel, Microstructure, Thermal cycles, granular bainite, acicular ferrite, M/A constituentاطلاعات بیشتر در مورد COI