Determination of the Nucleation and Crystallization Parameters for Making Nanoporous Titanium Phosphate Glass-ceramics
محل انتشار: مجله سرامیک های پیشرفته، دوره: 3، شماره: 3
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 179
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-3-3_005
تاریخ نمایه سازی: 11 اردیبهشت 1400
چکیده مقاله:
Nanoporous glass-ceramics were prepared with composition ۴۵CaO-۲۵TiO۲-۳۵P۲O۵ (mol%). Two molar percent of Na۲O was added as a flux to the composition. With the aforementioned composition, glass melted and crystallized into glass-ceramics containing β-Ca۳(PO۴)۲ and CaTi۴(PO۴)۶ as the main phases. The differential thermal analysis (DTA) was conducted to determine the suitable temperatures for nucleation and crystallization. Various times were examined for nucleation and the best nucleation time was chosen. The microstructure of final nucleated sample was observed by Scanning Electron Microscopy (SEM). Then, the glasses were crystallized and identified by X-ray Diffraction (XRD).The microstructures of crystallized specimens were studied by SEM.The glass-ceramics were leached in HCl, resulting β-Ca۳(PO۴)۲ was dissolved out leaving a porous structure as CaTi۴(PO۴)۶. It was found that specific surface area and average pore size diameter of the nanoporous glass-ceramics were controlled by the correct choice of heat treatment parameters. Using the optimal conditions for the production of nanoporous glass-ceramics with minimum pore size, ۲۶ m۲ and ۱۲.۳ were obtained for the specific surface area and pore diameter, respectively.
کلیدواژه ها:
نویسندگان
Farshad Soleimani
Material Engineering, Malayer University
Mohammad Rezvani
Materials Science & Engineering, Tabriz University
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :