Direct Drive Friction Welding Joint Strength of AISI ۳۰۴

  • سال انتشار: 1400
  • محل انتشار: ماهنامه بین المللی مهندسی، دوره: 34، شماره: 3
  • کد COI اختصاصی: JR_IJE-34-3_016
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 254
دانلود فایل این مقاله

نویسندگان

A. Jabbar Hassan

LMA, USTHB, BP. ۳۲, El-Alia, ۱۶۱۱۱ Bab-Ezzoaur, Algiers, Algeria

T. Boukharouba

LMA, USTHB, BP. ۳۲, El-Alia, ۱۶۱۱۱ Bab-Ezzoaur, Algiers, Algeria

D. Miroud

LSGM, USTHB, BP. ۳۲; El-Alia, ۱۶۱۱۱ Bab-Ezzouar, Algiers, Algeria

N. Titouche

DE M E M, DTN, Centre de Recherche Nucléaire de Birine, BP. ۱۸۰, Ain Oussera, Djelfa, Algeria

S. Ramtani

CSPBAT–LBPS, UMR ۷۲۴۴ CNRS, Paris University, Galilée Institute, Villetaneuse, France

چکیده

The present study describes the effect of friction welding process on mechanical and metallurgical properties of AISI ۳۰۴ steel. The joints were made by direct drive friction welding (DDFW) machine, while the characteristics of friction welded joints were evaluated by macro-microstructure, microhardness, tensile test with ۴ mm and ۶ mm effective diameter, and scanning electron microscope (SEM). The results showed severe flash formation at stationary side related to rotating side, highly plastically deformed zone (HPDZ) was revealed at the interface with large dimension of ۱۱۰ µm. Maximum microhardness values were recorded at welded center and increased from peripheral to central zones. Reducing ratio of ultimate tensile strength (UTS) and ductility for welded joint related to AISI ۳۰۴ were ۸۶ and ۶۷%, respectively. Tensile fractures occurred adjacent to the interface at thermo-mechanically affected zone (TMAZ). Fracture morphologies by SEM were discovered cleavage features and mostly ductile mode with micro-porosities of different forms and dimensions

کلیدواژه ها

Austenitic stainless steel, Micro-hardness, Ultimate Tensile Strength

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.