Experimental Study on Warm Incremental Tube Forming of AA۶۰۶۳ Aluminum Tubes
- سال انتشار: 1399
- محل انتشار: ماهنامه بین المللی مهندسی، دوره: 33، شماره: 9
- کد COI اختصاصی: JR_IJE-33-9_011
- زبان مقاله: انگلیسی
- تعداد مشاهده: 357
نویسندگان
Department of Mechanical Engineering, Kar higher Education Institute, Qazvin, Iran
Department of Mechanical Engineering, University of Birjand, Birjand, Iran
Department of Mechanical Engineering, Faculty of Enghelab-e Eslami, Tehran Branch, Technical and Vocational University (TVU), Tehran, Iran
چکیده
Effect of temperature on formability of AA۶۰۶۳ aluminum tubes in incremental forming process was investigated. Experiments are performed on AA۶۰۶۳ aluminum tubes. A spirally moving tool incrementally expands the tube wall. The tube is clamped from both ends while the deformation zone is not in contact with the die. A circumferential heating system is used to heat the tube due to the low formability of aluminum alloys at ambient temperature. The effects of process parameters including temperature, radial feed, axial feed and tool linear velocity are investigated in order to obtain the highest formability and surface quality. The results show that with a temperature rise from ۱۰۰°C to ۳۰۰°C, the expansion ratio increases from ۲۸% to ۳۴%. Axial feeding and temperature are the most effective parameters on the surface roughness and bulge diameter, respectively.کلیدواژه ها
Warm incremental tube forming, Expansion Ratio, Surface roughness, Temperatureاطلاعات بیشتر در مورد COI