Investigation of the cause of failure and knifeline attack in the welds of tubes of the direct reduction unit's recuperator
- سال انتشار: 1399
- محل انتشار: سومین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب ایران، بیست و یکمین کنفرانس ملی جوش و بازرسی و دهمین کنفرانس ملی آزمایش های غیرمخرب
- کد COI اختصاصی: INCWI21_033
- زبان مقاله: انگلیسی
- تعداد مشاهده: 418
نویسندگان
Bachelor graduate, Department of Materials Engineering - Isfahan University of Technology
Assistant Professor, Department of Materials Engineering - Isfahan University of Technology
Assistant Professor, Department of Materials Engineering - Isfahan University of Technology
PhD in material science and engineering at (MSE)Co.
چکیده
In this study, failure causes of the welding side area of austenitic stainless steel pipes AISI۳۲۱ of the direct reduction unit’s recuperator were investigated. The main problemwas the impossibility of replacing the pipes after the fracture. For this purpose, the cracks created in the pipes were repaired by filler metal ER۳۴۷ and ERNiCr-۳ using the melting welding method (GTAW). The microstructures of base and weld metals were evaluated by light and scanning electron microscopes using a reverse detector. The cracks are knife attack grooves created next to the weld and about ۳ to ۵ mm in the weld area. The results showed that the way to prevent cracks is to modify the welding method by selecting the appropriate parameters and inlet temperature. It was found that the use of ERNiCr-۳ filler metal to repair cracks due to having sufficient amounts of alloying elements can have optimal metallurgical properties and Improves working life and does not cause Sensitivity in the base metal.کلیدواژه ها
fracture, knife attack, failure analysis, structureمقالات مرتبط جدید
- Young’s modulus and Poisson’s ratio of enhanced re_entrant
- Vibrations Analysis of star-shaped auxetic plate using the Differential Quadrature Method
- Uterine and ovarian tissue engineering
- Type -I hot corrosion behavior of Cr -modified slurry alumini de coating superalloy Rene ۸۰
- Synthesis and characterization of temperature-sensitive smart hydrogel of polyethylene glycol
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.