Investigation of microstructure and tensile strength of TLP in the joint of AA2024-T4 alloys to AA6061-T6 using Sn-2.4Bi interlayer
- سال انتشار: 1399
- محل انتشار: سومین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب ایران، بیست و یکمین کنفرانس ملی جوش و بازرسی و دهمین کنفرانس ملی آزمایش های غیرمخرب
- کد COI اختصاصی: INCWI21_032
- زبان مقاله: انگلیسی
- تعداد مشاهده: 403
نویسندگان
Department of Materials Engineering - South Tehran Branch, Islamic Azad University, Tehran, Iran
Department of Materials Engineering - Karaj Branch- Islamic Azad University, Karaj, Iran
Department of Materials Engineering - South Tehran Branch, Islamic Azad University, Tehran, Iran
چکیده
AA2024-T4 and AA6061-T6 alloys were joined by diffusion bonding. 50μm tick Sn-2.4Bi foil was used as interlayer. Specimens with dimension of 130×32×3mm for strength test and 16×25×3mm for metallography were prepared by cutting. The bonding surfaces alloys prepared with 80 grit SiC finish. Alloys and interlayers were cleaned in ultrasonic bath of acetone for 10 min. Diffusion bonding was conducted in an atmosphere control tube furnace with heating rate of 5oC/min under argon gas at 2 atmospheres andat 253oC for 150,180, and 210 minutes for 50μm tick Sn-2.4Bi interlayer. Tensile strength of the joint after 210 min for 50μm tick Sn-2.4Bi interlayer was 12.3MPa. Jointswere observed and examined using SEM and mapping Element. Bi is distributed homogeneously in two base metal. Cu and Mg elements penetrated more than Al in theinterlayer.کلیدواژه ها
Transient Liquid Phase; Soldering; Diffusion bonding; Aerospace alloysمقالات مرتبط جدید
- Young’s modulus and Poisson’s ratio of enhanced re_entrant
- Vibrations Analysis of star-shaped auxetic plate using the Differential Quadrature Method
- Uterine and ovarian tissue engineering
- Type -I hot corrosion behavior of Cr -modified slurry alumini de coating superalloy Rene ۸۰
- Synthesis and characterization of temperature-sensitive smart hydrogel of polyethylene glycol
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.