Fabrication and characterization of magnesium-zinc scaffolds with nano structure calcium phosphate coating by pulse electro deposition

سال انتشار: 1399
محل انتشار: پنجمین کنفرانس بین المللی تحقیقات پیشرفته در علوم، مهندسی و فناوری
کد COI اختصاصی: RSETCONF05_019
زبان مقاله: انگلیسی
تعداد مشاهده: 322

نویسندگان

Nanotechnology department, Faculty of Engineering, University of Guilan, Rasht, Iran,

Nanotechnology department, Faculty of Engineering, University of Guilan, Rasht, Iran

چکیده

Mg and its alloys are biodegradable, mechanically strong, and promising for an orthopedic implant and device applications. However, currently available degrade too rapidly to meet clinical needs. Therefore, an effective way to reduce the rate of scaffold degradability is coating.The aim of this study is to investigate the effect of pulse electrodeposition parameters such as peak current density and duty cycle on surface characteristics of nano structure calcium phosphate coating on theporous Mg- ۲Zn (wt.%) scaffold. Pulse deposition electrode method was used to produce the coating of nano calcium phosphate. Mg-۲Zn (wt.%) porous alloys were prepared using a powder metallurgical process.The results showed that the optimum conditions to create uniform coating on the Mg-۲Zn scaffold are at ۴۰ mA/cm۲ peak current density, ۰.۲ duty cycle , ۲h time coating consists of Hydroxyapatite andBrushite with needle-like (which exhibits a similar composition of natural bone) and plate-like structures under optimum conditions

کلیدواژه ها

Magnesium-Zinc-Porous bone metal scaffold-Pulse electro deposition- Nano structure calsium phosphate

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.