Evaluation of the effect of 4 wt.% Si and 1 wt.% Mg addition on solidification, microstructure, mechanical and wear properties of Al-15Sn bearing alloy
سال انتشار: 1399
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 340
فایل این مقاله در 14 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES14_001
تاریخ نمایه سازی: 1 دی 1399
چکیده مقاله:
Al-Sn bearing alloys, despite their excellent anti-friction properties, have limited use due to their low-load bearing capacity and low-fatigue resistance. In this study, it has been tried to eliminate some of these limitations by adding4 Wt. % Si and 1 Wt. % Mg elements to Al-15Sn alloy. Thermal analysis of the new alloy showed a eutectic reaction during the solidification path after a primary precipitation and a monotectic reaction. The microstructural evaluations of the new alloy showed a change from a networked Sn phase around the primary α-Al dendrites to the peritectic-type island structure. The results of mechanical tests showed with the addition of Si and Mg, elastic modulus increased about 5.8 times, the compressive yield strength increased about 7.7 times and the hardness increased about 2 times. The results of the wear test also showed an increase in the friction coefficient of about 33% and a decrease in weight loss of about 10%.
کلیدواژه ها:
نویسندگان
Majid Daneshzadeh
Master, Department of Materials and Polymer Engineering, Hakim Sabzevari University, Sabzevar, P.O. Box: ۳۹۷, Iran
Bahman Korojy
Assistant Professor, Department of Materials and Polymer Engineering, Hakim Sabzevari University, Sabzevar, P.O. Box: ۳۹۷, Iran