Isothermal Recrystallization Behavior of Cold-deformed Martensite in an Ultra-low-carbon Microalloyed Steel
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 329
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-16-1_001
تاریخ نمایه سازی: 10 آذر 1399
چکیده مقاله:
One of the most promising ways to produce a grain-refined microstructure in some steel materials is the thermomechanical processing route of subcritical recrystallization annealing of a cold-deformed martensite structure. In the present study, the microstructural evolutions and the associated recrystallization kinetics under various subcritical annealing heat treatment conditions are explored in an API X120 grade, advanced, High-Strength, Low-Alloy (HSLA) steel with an initial cold-deformed martensite microstructure. The steel sheet was the subject of a conventional cold rolling process for moderate true strain of 60% followed by isothermal recrystallization for different temperature-time combinations. Optical microscopy and scanning electron microscopy were used to characterize the microstructural evolutions, and the recrystallization kinetics was evaluated by hardness measurements with the aid of the Johnson-Mehl-Avrami-Kolmogorov (JMAK) relationship. The experimental results indicated that annealing at 948 K (675 °C) for 18 h is the optimum condition to achieve a grain-refined ferrite microstructure with an averaged grain size of 5.2 µm. The slow kinetics of recrystallization was also revealed by JMAK model as the Avrami exponent was calculated around one for all of the experiments. These observations are rationalized in part by the possible formation of microalloying elements carbides during the annealing process in association with the existence of the inhomogeneously deformed initial microstructure. This results in the appearance of a continuous regime for the recrystallization nucleation along with the sluggish movement of recrystallization fronts.
کلیدواژه ها:
نویسندگان
A. Ghorabaei
Advanced Phase Transformations Laboratory (APTL), School of Metallurgy and Materials Engineering, University of Tehran, Tehran ۱۴۳۹۵-۵۱۵, Iran
محمود نیلی احمدآبادی
Advanced Phase Transformations Laboratory (APTL), School of Metallurgy and Materials Engineering, University of Tehran, Tehran ۱۴۳۹۵-۵۱۵, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :