Effects of micro and nano-silica on the fresh and hardened properties of self- consolidating concrete

سال انتشار: 1399
محل انتشار: کنفرانس بین المللی عمران، معماری، توسعه و بازآفرینی زیرساخت های شهری در ایران
کد COI اختصاصی: ICDU01_104
زبان مقاله: انگلیسی
تعداد مشاهده: 484

نویسندگان

Department of Civil Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran

چکیده

This experimental study was conducted in order to investigate the properties of self-consolidating concrete (SCC) containing microsilica (Ms) and nanosilica (Ns). Accordingly, five types of SCC mixes were made with a w/b ratio of 0.45 as well as different percentages of Ms and Ns. In this study, replacement ratios 10% of Ms and 1, 2, or 3% of Ns were considered. The obtained results revealed that the using of 10% Ms reduced the water penetration depth of the SCC up to 51% and increased the 28-day compressive strength of SCC by 16% compared to the control sample. Also, 2% Ns had the most impact on the water penetration depth and compressive strength of the SCC compared to other percentages of Ns. as result, applying 10% Ms has a higher effect on compressive strength and the water permeability compared to Ns.

کلیدواژه ها

SCC; compressive strength; water permeability; nano-silica; micro-silica

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.