Synthesis and characterization of 13X zeolite powder

  • سال انتشار: 1389
  • محل انتشار: اولین همایش ملی توسعه تکنولوژی در صنایع نفت، گاز و پتروشیمی
  • کد COI اختصاصی: TOIL01_162
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 3331
دانلود فایل این مقاله

نویسندگان

Toraj Mohammadi

Islamic Azad University, South Tehran Branch, Department of Chemical Engineering

Majid Badini Pour Azar

Tehran Refinary (Shahid Tond Gooyan), National Oil Product and Distillation Co., Tehran

Mansoor Kazemi Moghadam

Islamic Azad University, South Tehran Branch, Department of Chemical Engineering

Omid Bakhtiari

Research Center for Membrane Separation Processes Department of Chemical Engineering, Iran University of Science and Technology (IUST), Narmak, Tehran,

چکیده

Zeolite 13X powders are of the major categories of zeolites and have a great potential to be employed industrially in many applications including gas separation tasks, e.g. CO2 and H S removal form natural gas by separation by adsorption, especially for CO2Effects of SiO2 /Al2 O3,H2 O/Na2O3and H2 O/SiO2 molar ratios was investigated on13X zeolite hydrothermal synthesis. Prepared powders was characterized using XRD analysis It was found that silica source, synthesis temperatures, and H O/Na O molar ratios are affecting parameters in zeolite13X synthesis and its crystalinity The best result was found for 1 Al2 O3;2.9 SiO2:4.35Na2O;304.5H2O at synthesis temperature of 110°C in5 h with aging time of 24 h.

کلیدواژه ها

zeolite 13X synthesis Silica source type, molar ratio, synthesis temperature,characterization

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.