Effect of Temperature and Atmosphere on the Thermal Degradation of Polyethylene
- سال انتشار: 1397
- محل انتشار: دومین کنفرانس دوسالانه بین المللی نفت، گاز و پتروشیمی
- کد COI اختصاصی: OGPC02_082
- زبان مقاله: انگلیسی
- تعداد مشاهده: 490
نویسندگان
Research and Development Center, Jam Petrochemical Company, Asalouyeh, Iran
Research and Development Center, Jam Petrochemical Company, Asalouyeh, Iran
Research and Development Center, Jam Petrochemical Company, Asalouyeh, Iran
چکیده
In this paper, a time-sweep rheometry method was used to evaluate the thermal degradation of a linear low density polyethylene. For this purpose, the rheometry was performed by time-sweep method in the air and nitrogen atmosphere. Storage modulus values were reported as a function of the time. According to the results, this method had a good repeatability. No degradation was observed under nitrogen atmosphere. The results showed that rheometry in presence of air caused a faster and more severe degradation of polyethylene. Higher temperatures shifted forward the onset of the degradation and caused the increase in the slope of the storage modulus-time curveکلیدواژه ها
Polyethylene, Time-Sweep Rheometry, Rheology, Thermal Degradationمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.