Synthesis Zr-Co-Y based chemical getter and evaluation its vacuum preserving, sorption characteristics, and hydrogen absorption

سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 354

فایل این مقاله در 14 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

JR_IJHFC-6-2_006

تاریخ نمایه سازی: 5 شهریور 1399

چکیده مقاله:

In this research, a Zr-Co based chemical non-evaporable getter (NEG) was synthesized via mechanical alloying. A mixture with a 75 %Wt. Zr, 22 %Wt. Co, and 3 %Wt. Y composition (Zr75Co22Y3) was selected, mixed, and milled up to 42 h. The obtained powder was pressed in a tablet form. The sample was placed in a well-sealed vacuum chamber that was evacuated to 1.5×10-5 mmHg. Then, the sample was subjected to different heat treatments (at various temperatures and times) for activation. Results revealed that the final vacuum for the Y36030 sample (Zr75Co22Y3 activated at 360ºC for 30 min) and the Y28030 sample (Zr75Co22Y3 activated at 280 ⁰C for 30 min) were 5.95×10-6 and 9.9×10-6 mmHg, respectively. After finishing the heat treatment, vacuum variation versus time was recorded in the range of 0.001-0.2 mmHg, the time for Y36030, Y28030, and a no-getter was 3088, 510, and 345 seconds, respectively. Sievert results showed that Y36030 absorbed 1.5 %Wt H2 at 45 bar while Y28030 absorbed 1.05 %Wt. H2. After removing the pressure, the remaining amount of hydrogen for Y36030 and Y28030 was 0.7 and 0.55 %Wt., respectively.

نویسندگان

Mehrdad Fattahzadeh

Department of Advanced Materials and Renewable Energies, Iranian Research Organization for Science and Technology, Tehran, Iran

Ali Kaflou

Department of Advanced Materials and Renewable Energies, Iranian Research Organization for Science and Technology, Tehran, Iran

valiollah Dashtizad

Department of Advanced Materials and Renewable Energies, Iranian Research Organization for Science and Technology, Tehran, Iran

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • Xu Y., Cui J., Cui H., Zhou H., Yang Zh., ...
  • SAES Getter, Technical Report, St 707 Non-Evaporable Getters Activatable at ...
  • Benvenuti C., Chiggiato P., Obtention of pressures in the 10−14 ...
  • Benvenuti C., Chiggiato P., Pumping Characteristics of the St707 Nonevaporable ...
  • Riabova A.B., Yartys V. A., Fjellvag H., Haubackb B.C., Sørbyb ...
  • Heidary Moghadam A., Dashtizad V., Kaflou A., Yoozbashizadeh H., Effect ...
  • Zhang H., Su R., Chen D., Shi L., Thermal desorption ...
  • Konishi S., Nagasaki T., Yokogawa N., Naruse Y., Development of ...
  • Penzhorn R.D., Devillers M., Sirch M., Evaluation of ZrCo and ...
  • Zavaliy I.Yu., Denys R.V., erný R. Cˇ, Koval’chuck I.V., Wiesinger ...
  • Xu Y., Cui J., Cui H., Zhou H., Yang Zh., ...
  • Bu J.G., Mao C.H., Zhang Y., Wei X.Y., Du J., ...
  • Valdre G., Zacchini D., Berti R., Costa A., Alessandrini A., ...
  • Neelima B., Rama Rao N.V., Rangadhara V., Pandian S., Influence ...
  • Sakintuna B., Lamari-Darkrim F., Hirscher M., Metal hydride materials for ...
  • Gregg S.J., Sing K.S.W., Adsorption, surface area and porosity . ...
  • Fattahzade. M, Kaflou. A, Dashtizad V., Study the Effect of ...
  • Huaqin Kou W.L., Huang Zh., Sang G., Hu Ch., Chen ...
  • Matolin V., Drbohlav J., Masek K. , Mechanism of non-evaporable ...
  • Batra I.S., Singh R.N., Sengupta P., Maji B.C., Madangopal K., ...
  • Heidary Moghadam A., Dashtizad V., Kaflou A., Yoozbashizadeh H., Ashiri ...
  • Petti, D., Cantoni. M., Leone M., Bertacco R., Rizzi E., ...
  • Dwight A.E., Klippert T.E., Variants of Zr3Co and their superconducting ...
  • Bereznitsky M., Jacob I., Bloch J., Mintz M. H., Thermodynamic ...
  • Fisher.P.W., Tanase M., Diffusivities of hydrogen in yttrium and yttrium ...
  • Hara M., Okabe T., Mori K., Watanabe K., Kinetics and ...
  • Szpunar J. A., Qin W., Li H., Kiran Kumar N.A.P., ...
  • Buschow K.H.J., Bouten P.C.P., Miedema A.R., Hydrides formed from intermetallic ...
  • Sandrock G., A panoramic overview of hydrogen storage alloys from ...
  • Zhang T., Zhang Y., Zhang M., Hu R., Kou H., ...
  • Asse-Coutrin N., Altenor S., Cossement D., Jean-Marius C., Gaspard S., ...
  • Altin O., Özbelge HÖ., Dogu T., Effect of pH in ...
  • Simon C. A., Scandium, Yttrium & the Lanthanides: Inorganic & ...
  • Tejland P., Andren H.O., Origin and effect of lateral cracks ...
  • Martin M., Gommel C., Borkhart C., Fromm E., Absorption and ...
  • Benvenuti C., Chiggiato P., Pinto P.C., Vacuum properties of TiZrV ...
  • Bakker H., Bonzel H.P., Bruff C.M., Dayananda M.A., Gust W., ...
  • نمایش کامل مراجع