Nano Coatings on AISI 430 to Reduce Cr2O3Growth for SOFC Interconnect Applications

سال انتشار: 1389
محل انتشار: اولین کنفرانس ملی علوم و فناوری نانو
کد COI اختصاصی: NNTC01_357
زبان مقاله: انگلیسی
تعداد مشاهده: 1813

نویسندگان

Kerman, Shahid Bahonar University, Department of Materials Science and Engineering

چکیده

The formation of oxide layer on the surface of used interconnects in solid oxide fuel cells (SOFCs), decrease the electrical conductivity and therefore energy losses can be occurred. The aim of this study was to compare the effect of two types of coating layer on the growth of chromia layer. AISI 430 ferri&c stainless steel was coated in a cobalt and manganese-base pack mixture by pack cementation, separately. Isothermal and cyclic oxida&on were applied at 800 °C to evaluate the oxide layer thickness. The cobalt coating transformed to MnCo2O4 and CoCr2O4 spinels during isothermal oxidation and manganese coating transformed to Mn3O4 and MnFe2O4nano spinels. Results showed that the increase of isothermal oxidation time and cycle number increased the oxide thickness. Also in each test the cobalt coating showed lower oxide thickness in comparison to the manganese coating.

کلیدواژه ها

chrimia (Cr2O3), AISI 430 stainless steel, nano spinel, oxide thickness, interconnects

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.