Sustainable development of Portland cement: Effect of different types of accelerators on the setting time

  • سال انتشار: 1399
  • محل انتشار: هفتمین کنفرانس ملی پژوهش های کاربردی در مهندسی عمران، معماری و مدیریت شهری و ششمین نمایشگاه تخصصی انبوه سازان مسکن و ساختمان استان تهران
  • کد COI اختصاصی: CEUCONF07_539
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 531
دانلود فایل این مقاله

نویسندگان

Sepideh Rahmati

Bachelor degree, Civil engineering department, Khomeinishahr Branch, Islamic Azad University, Khomeinishahr,Isfahan, Iran

Ali Hendi

Instructor, Civil engineering department, Khomeinishahr Branch, Islamic Azad University, Khomeinishahr, Isfahan,Iran

Sattar Ahmadifar

Bachelor degree, Civil engineering department, Khomeinishahr Branch, Islamic Azad University, Khomeinishahr,Isfahan, Iran

Mohammad Javad Pourheydar

Bachelor degree, Civil engineering department, Khomeinishahr Branch, Islamic Azad University, Khomeinishahr,Isfahan, Iran

Mohammad Reisi

Assistant professor, Civil engineering department, Khomeinishahr Branch, Islamic Azad University, Khomeinishahr,Isfahan, Iran

Bachelor Degree

چکیده

Cement should be partially replaced by supplementary cementitious materials to reduce the environmental impact of itsproduction. Generally, this replacement increases the setting time of Portland cement, which leads to the formation ofcracks on the concrete surface, and consequently, a reduction in concrete durability. To overcome this issue, the effectof different types of accelerators on the initial and the final setting time of Portland cement was investigated. Resultsindicated that the ultimate behavior of calcium chloride and sodium silicate on the setting time were almost the same.These substances were very effective on the reduction of the final setting time of cement at low substitution dosage,while the initial setting was marginally reduced. Aluminum sulfate, in contrast, had a substantial impact on the initialsetting time at low dosages while all of the accelerators reduced initial and final setting time at high substitutiondosage.

کلیدواژه ها

Aluminum sulfate; Calcium chloride; Sodium silicate; Sustainable development, Setting time, Accelerator

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.