Synthesis of CaO nano particles via precipitation in ethanol
- سال انتشار: 1389
- محل انتشار: اولین کنفرانس ملی علوم و فناوری نانو
- کد COI اختصاصی: NNTC01_057
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2203
نویسندگان
Iran, Urmia, Urmia University of Technology, Chemical Engineering Facaulty
Iran, Urmia, Urmia University of Technology, chemical Engineering Facaulty
چکیده
Nanosized CaO powder was prepared via sol–gel precipitation in ethanol followed by a washingdrying treatment and calcination. The reactant concentration, the molar ratio of reactants and the calcinations temperature were inspected by homogenous design. TEM, XRD and SEM were used to characterize the products. The experimental results showed that ethanol can avoid hard agglomerate during precipitation and that calcinations temperature was the major factor to determine the surface area, the diameter and the phase composition of the final product. When the calcina)on temperatures were controlled between 686–1029 °C, the agglomerate-free nano-sized CaO particles with a size range of 5–9 nm were obtainedکلیدواژه ها
CaCl2, Tem, XRD, hydrolyzation, nanoparticleمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.