Effect of temperature and composition on the cell morphology and the density of polystyrene / polymethyl methacrylate blend foams

سال انتشار: 1399
محل انتشار: ششمین کنفرانس بین المللی نوآوری و تحقیق در علوم مهندسی
کد COI اختصاصی: ICIRES06_036
زبان مقاله: انگلیسی
تعداد مشاهده: 470

دانلود فایل این مقاله

نویسندگان

Davoud Jahani

Mechanical Engineering Department University of Bonab Bonab, Iran

Amin Nazari

Chemical Engineering Department University of Maragheh Maragheh, Iran

Hassan Mansoori

Aerospace Engineering Department K. N. Toosi University of Technology Tehran, Iran

چکیده

In this paper, the foaming process and cell morphology of polystyrene(PS)/ polymethyl methacrylate(PMMA) blend foams were studied. PS / PMMA blends were prepared in different compositions with /without calcium carbonate. In order to investigate the foaming process, the polymer plates samples, 200 μm in thick, were saturated with normal pentane gas and foaming process was studied. The results show that with increasing of the temperature, the saturation process performs faster. Also with the increase of PMMA content in the blend, the gas penetration into the polymer and foam density decreases. Addition of nanoparticles in the blend resulted on increasing of the nucleation rate and void density.

کلیدواژه ها

Nano particle; Foam; Polystyrene

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.