Synthesis of Lead Titanate Nanostructure by Mechanical Activation Method and Evaluating of its Photocatalytic Decolorization of Methyl orange
محل انتشار: مجله مواد دوستدار محیط، دوره: 4، شماره: 1
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 242
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JEFM-4-1_003
تاریخ نمایه سازی: 1 مرداد 1399
چکیده مقاله:
In this study, lead titanate nanopowder was synthesized using mechanical activation. Raw materials including titanium oxide powder (anatase) and Lead oxide (ІІ) with a ball to powder weight ratio of 1: 10 and the powder ratio of 1:1 were milled in a planetary ball mill for 30 hours. Then, they were heated at 800, 900 and 1000 °C. The volatility of lead and the formation of secondary phases were prevented using this method. The obtained nanopowder was investigated by field emission scanning electron microscope (FESEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). The UV absorption spectroscopy was used to calculate the energy gap. Photocatalytic activity of nanopowder by dye degradation of methyl orange under UV light was evaluated. The effects of various influential parameters including initial dye concentration, photocatalyst dose and pH on the dye decolorization were also investigated. The optimum value for initial dye concentration and photocatalyst dose, obtained 10 ppm and 0.042 g, respectively. Also, the best rate of decolorization observed at pH=4. The results suggested that photocatalytic process is a beneficial method for decolorizing methyl orange dye.
کلیدواژه ها:
نویسندگان
E Khosravipanah
Department of Materials Engineering, Shahrood Branch, Islamic Azad University, Shahrood, Iran
S, A Manafi
Department of Materials Engineering, Shahrood Branch, Islamic Azad University, Shahrood, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :