The investigation on the role of nano sized calcium carbonate particles in a MDPE on its resistant against perforation
- سال انتشار: 1389
- محل انتشار: دومین کنفرانس بین المللی کامپوزیت
- کد COI اختصاصی: COMPOSIT02_165
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1382
نویسندگان
Graduate student
Associated Professor
Assistant Professor
Graduate student,Department of Materials Science and Engineering Ferdowsi University Of Mashhad, Mashhad,Iran
چکیده
In this article, the role of nano size calcium carbonate on resistant against penetration and perforation of MDPE was investigated through experiments. The results of perforation tests showed that the tearing behaviour of MDPE/CaCO3 nanocomposites depends on their relative amount of CaCO3 particles. Addition of CaCO3 nanoparticles to pure PE increased both the applied force for the first penetration of the indenter in the sample and the peak force (perforation force). In addition, this nanocomposite sample consumed the greatest energy for the whole perforation test. The plastic zone regions around the perforated area were inspected using scanning electron microscopy. The toughening mechanisms of shear yielding and massive shear yielding observed. The mechanical response of composite samples containing CaCO3 nanoparticles greater than 5 wt.% in a perforation test was found to be different. Fracture surface images showed when calcium carbonate content is higher than 5 weight percent, agglomeration of nano particles occured. Debonding stress relates on particle size inversely and debonding stress will be raised as particle size decreases. Therefore, as shown in the SEM micrograph of a nanocomposite sample with 10 wt.% CaCO3 nanoparticles, the crack has been nucleated and then propagated during different stages of the test.کلیدواژه ها
Polyethylene, Calcium Carbonate, Perforation, agglomeration, Debondingمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.