Structure and Glass Transition Temperature of PMMA/Clay nanocomposites synthesized through in situ-Reversible Addition- Fragmentation Transfer (RAFT) Polymerization
- سال انتشار: 1389
- محل انتشار: دومین کنفرانس بین المللی کامپوزیت
- کد COI اختصاصی: COMPOSIT02_143
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1502
نویسندگان
Department of Chemical Engineering, Faculty of Engineering, University of Isfahan, P. O. Box ۸۱۷۴۶-۷۳۴۴۱, Isfahan, Iran
Department of Chemical Engineering, Faculty of Engineering
چکیده
In this research poly(methyl methacrylate)/clay nanocomposite was prepared through reversible additionfragmentation transfer (RAFT) polymerization. Two synthesized RAFT agents, 3-(morpholino-4- carbothioylsulfanyl)-propionic acid methyl ester (RAFT-І) and diethyl-dithiocarbamic acid 2-carbamoyl-ethyl ester (RAFT-ІІ) were used. The morphology of samples was determined with X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results indicated the proper intercalation of polymer chains between silicate layers. Dynamic mechanical thermal analysis (DMTA) was also used to determine the glass transition temperature (Tg) of samples. It was found that Tg is reduced in nanocomposites relative to that in neat polymerکلیدواژه ها
poly(methyl methacrylate), nanocomposite, RAFT polymerization, glass transition temperature,morphologyمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.