Synthesis of alumina-mullite nanopowder using AlCl3.6H2O & colloidal silica via Sol–gel method

  • سال انتشار: 1389
  • محل انتشار: دومین کنفرانس بین المللی کامپوزیت
  • کد COI اختصاصی: COMPOSIT02_042
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 1412
دانلود فایل این مقاله

نویسندگان

A Sedaghat

Ph.D. student

E aheri-Nassaj

Professor, Department of Materials Science and Engineering, Tarbiat Modares University

G.D Soraru

,۳Professor, Departmentof Materials Engineering and Industrial Technology, University of Trento

R Ceccato

Professor, Materials & Energy Research Centre, PO Box ۱۴۱۵۵-۴۷۷۷, Tehran, Iran

چکیده

Via sol-gel method, it can be obtained, the homogeneous distribution of mullite in alumina matrix. In this work, alumina-mullite nanopowder was synthesized by aluminium chloride hexahydrate and colloidal silica via sol-gel method and in the other works it had been prepared by alumina and TEOS. According to the XRD patterns of alumina-mullite 15%vol. precursors calcined at different temperatures, transitional alumina (γ, κ) & silica phases (quartz, tridymite) crystallize at around 900°C. Then it transforms to α alumina & mullite in the range of 1000-1300°C completely. Specific surface area and density of the nanopowder calcined at 900oC are 105.4 ± 0.4 m2/g & 3.646 ± 0.007 g/cm3 respectively. Then the nanopowder was observed by TEM.

کلیدواژه ها

Nanopowder; Alumina; Mullite; Sol-gel processes; Phase transformation

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.