A Study on the fracture behavior of polyethylene/calcium carbonate nanocomposites using the essential work of fracture (EWF) method
- سال انتشار: 1389
- محل انتشار: دومین کنفرانس بین المللی کامپوزیت
- کد COI اختصاصی: COMPOSIT02_037
- زبان مقاله: انگلیسی
- تعداد مشاهده: 2528
نویسندگان
Graduate student
Professor
professor ,Department of Materials Science and Engineering
چکیده
In the case of ductile materials such as thin plastic films, the applied stress state in front of the crack tip is in a plane stress condition and the deformation around the crack tip is very large. Thus linear elastic fracture mechanics (LEFM) can not be employed to elucidate the fracture behavior of such materials.Recent studies have shown that the essential work of fracture (EWF) method can be a very useful tool for studying the fracture properties of thin films particularly of ductile films. In the current research, the fracture behavior of polyethylene (PE) films including pure and reinforced with different content of nano size calcium carbonate was investigated by means of EWF method under mode I loading. For this purpose deeply double edge notched (DDEN) specimens with ligament lengths ranging from 5 to 15 mm cut from compression molded films and subjected to tensile tests at a constant crosshead speed of 5 mm/min. The essential (we) and non-essential work of fracture (βwp) were estimated from plots of the specific total work of fracture (wf) versus ligament length. The fracture surfaces of MDPE and nanocomposites were studied by scanning electron microscopy (SEM). The results showed that we of PE/CaCO3 nanocomposites was lower than that of neat PE, while βwp increased with increasing CaCO3 content up to 2.5wt%, and then decreased for the nanocomposites containing 5wt% CaCO3. The observed trend in the toughness parameters (i.e. we) was well demonstrated by the microscopic evaluation.کلیدواژه ها
Essential work of fracture (EWF); Nanocomposite; Polyethylene; CaCO3مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.