The Room-Temperature Sodium-Free Organosol Precipitation of Barium Titanate Nanocrystals
محل انتشار: مجله سرامیک های پیشرفته، دوره: 5، شماره: 2
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 272
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-5-2_003
تاریخ نمایه سازی: 24 فروردین 1399
چکیده مقاله:
The purpose of this research was to produce high-purity monodisperse barium titanate nanocrystals (BTO-NCs). To this end, a modified and very high-yield organosol precipitation method was developed. The novelty of this method was its purely organic approach, which stoped the application of inorganic bases such as caustic soda (NaOH) and avoided the risk of the presence of undesirable ions in the synthesized dielectric material. Results showed that an absolutely-organic base, such as the methylamine aqueous solution could ensure the basic condition required for high-yield organosol precipitation. X-ray diffraction, scanning electron microscopy, dynamic light scattering, and high-resolution transmission electron microscopy analyses were utilized to ensure the formation of monodisperse NCs. It was also found that monodisperse precursor crystals of about 3 nm have been achieved. Using oleic acid as the capping agent allowed generating uniformly small size and excellent dispersibility of the precipitate in the nonpolar solvents. Thus, the synthesized NCs could be easily redispersed in different nonpolar solvents to produce various suspensions of nm-size BTO-NCs without adding any surfactant. The obtained transparent suspensions, which include well-dispersed nm-size crystals, are promising for many applications in nanotechnology such as advanced electro-optic devices.
کلیدواژه ها:
نویسندگان
Abolghasem Nourmohammadi
Department of Nanotechnology Engineering, Faculty of Advanced Science and Technologies, University of Isfahan, Isfahan, Iran
Doru C. Lupascu
Institute for Materials Science and Center for Nanointegration Duisburg-Essen (CENIDE), University of Duisburg-Essen, ۴۵۱۴۱ Essen, Germany
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :