Micro-Thermal Residual Stress Concentration in Three-Phase Fiber-Reinforced Composites

In the present research, curing micro-residual stress concentration in polymer composites is predictedtheoretically. For this purpose, a three phase composite has been considered includes fiber, matrix as well as the interphase between them. First, a review on the available three-dimensional energy method based analytical solutionfor micro-thermal residual stresses is presented. Analytical results show that a shear stress concentration occurs at vicinity of composite edge that jumps importantly due to a decrease in interphase thickness. Imperfect adhesion hasless stress concentration in comparison with perfect bonding conditions. High mismatch in coefficient of the thermal expansion and Young’s modulus of the fiber and matrix affect the shear stress distribution along the fiber length,especially near the fiber ends, while the difference between the Poisson’s ratios of the composite constituents has not any significant role.

کلیدواژه ها:

Micro-Residual Stress ، Energy Method ، Shear Stress Concentration ، Interphase